Immobilization of simulated low and intermediate level waste in alkali-activated slag-fly ash-metakaolin hydroceramics

In the current study, the alkali-activated slag-fly ash-metakaolin hydroceramic (ASFMH) waste forms for immobilizing simulated low and intermediate level waste (S-LILW) were prepared by hydrothermal process. The crystalline phase compositions, morphology, compressive strength and aqueous stability of S-LILW ASFMH waste forms were investigated. The results showed that the main crystalline phases of S-LILW ASFMH waste forms were analcime and zeolite NaP1. The changes of Si/Al molar ratio (from 1.7 to 2.2) and Ca/Al molar ratio (from 0.15 to 0.35) had little effect on the phase compositions of S-LILW ASFMH waste forms. However, the hydrothermal temperature, time as well as the content of S-LILW (from 12.5 to 37.5 wt%) had a major impact on the phase compositions. The compressive strength of S-LILW ASFMH waste forms was not less than 20 MPa when the content of S-LILW reached 37.5 wt%. In addition, the aqueous stability testing was carried out using the standard MCC-1 static leach test method; the normalized elemental leach rates of Sr and Cs were fairly constant in a low value below 5 × 10−4 g m−2 d−1 and 3 × 10−4 g m−2 d−1 after 28 days, respectively. It is indicated that ASFMH waste form could be a potential host for safely immobilizing LILW.