•Corrosion performance of coated steel by UV-cured formulations was investigated.•Impedance spectroscopy was used to evaluate the corrosion protection.•A newly synthesized phosphonated fatty acid was added to the formulation as corrosion inhibitor.•Coating performance increased in the presence of the new additive.
Six formulations containing diacrylate monomers (from 89 to 92.5% (w/w)) as well as a phosphonated methacrylate monomer (from 1 to 10% (w/w)) were prepared. All formulations were UV-cured and the corrosion performance of the resulting coatings applied onto a steel substrate was assessed by electrochemical impedance spectroscopy (EIS). It was first shown that the coatings containing phosphonic acid methacrylate (MAPC1(OH)2) instead of methacrylate phosphonic dimethyl ester (MAPC1) presented higher corrosion protection related to the strong adhesive properties of phosphonic acid on the metal substrate. A minimum MAPC1(OH)2 content of 2.5% was determined to provide the highest impedance values (best efficiency). Then, a new bio-based compound, i.e. phosphonic acid-bearing oleic acid (phosphonated fatty acid), was synthesized and added as an inhibitor to the formulations. In the presence of this compound, the corrosion protection was notably improved. The beneficial effect of phosphonated fatty acid was explained by its inhibitive action at the steel/coating interface and by the improvement of the barrier properties.