| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 7005291 | Wear | 2012 | 13 Pages |
Abstract
⺠Thermal stresses developed during spraying were main causes for presence of micro-cracks in the coatings. ⺠For the highest adhesion values, coating failure was mainly located in the bond coat/substrate interface. ⺠Erosion wear was more at 45° angle of impact showing that erosion behavior as a composite ductile-brittle. ⺠Erosion of coating systems occurred through spalling of lamella exposed on coating surface resulting from cracking along the lamellar interface.