Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
7119688 | Materials Science in Semiconductor Processing | 2014 | 6 Pages |
Abstract
Mg-Al co-doped ZnO thin films were prepared via radio-frequency reactive magnetron sputtering technique. X-ray diffraction investigation showed all the thin films with different Mg:Al ratio had hexagonal wurtzite structure. All the thin films showed (100) preferential orientation of ZnO. When Al concentration was kept constant but Mg concentration was increased, the grain size decreased at first and then increased. When Mg:Al ratio was 3:1, the grain size reached a maximum. Ultraviolet-visible spectra showed the thin films had a high average transmittance of 80% in the visible range. The optical band gaps of the thin films were obtained as follows: 3.31, 3.32, and 3.37Â eV, corresponding to the Mg:Al ratio of 0:1, 1:1, and 3:1, respectively. Photoluminescence spectroscopy showed all the thin films had four main peaks located at 386, 410, 463, and 499Â nm. The origin of blue peak is oxygen vacancy. When Mg concentration was kept constant but Al concentration was increased, I-V curve presented that for both of the heterojunctions the rectifying behavior was formed. The conductivity of Mg:Al=1:1 thin film is higher than that of Mg:Al=1:0 thin film. After illumination, light I-V curve deviated from rectifying character.
Keywords
Related Topics
Physical Sciences and Engineering
Engineering
Electrical and Electronic Engineering
Authors
C.Y. Wang, S.Y. Ma, F.M. Li, Y. Chen, X.L. Xu, T. Wang, F.C. Yang, Q. Zhao, J. Liu, X.L. Zhang, X.B. Li, X.H. Yang, J. Zhu,