7167549 | Engineering Failure Analysis | 2018 | 12 Pages |
Abstract
The secondary crack is located near the main crack as per the macro examination and micro analysis on the fracture of a PDM (Positive Displacement Motor) shell with special taper thread, and serious defects are produced at the bottom of thread surface in the process of main crack fracture. Scanning electron microscopy observation indicates that the shear fracture point is positioned at shear fracture zone and convex of thread bottom tearing crack of sample 1#. Based on field data and type design of special thread, the matching model of special taper thread of cardan shaft shell is established in this paper, and numerical simulation of threaded connection is carried out under three different borehole curvatures. Results indicate that stress and displacement of thread increase with the borehole curvature. When the curvature reaches 30°/30 m, the maximum Von Mises stress is 967.8 MPa, which is close to the yield stress of thread material. The maximum stress occurs at the bottom of the first tooth according to the actual fracture location. Comprehensive analysis reveals that the effect of bending load occurs many times at the bottom of well. Moreover, thread surface defects result in large stress of thread, and form the weakest micro cracks at the bottom of thread. In addition, the crack occurs in the smooth area, and then rapidly extends to the shear lip, which leads to failure and even fracture of threaded connection of shell.
Related Topics
Physical Sciences and Engineering
Engineering
Industrial and Manufacturing Engineering
Authors
Yang Liu, Zhanghua Lian, Liqin Qian, Chengyu Xia, Jie Zhang, Yiliu Tu,