Measure of fracture toughness of compressive fiber failure in composite structures using infrared thermography

Compressive fiber failure in unidirectional composite laminate has been chosen due to its difficulty to evaluate toughness. Infrared thermography has been employed to follow compressive failure mode developing during an indentation test and a compression after impact test, and to evaluate the fracture toughness of compressive fiber failure. The obtained results show a good correspondence with the value found in a previous work on FE analysis of impact damage and are consistent with the literature.