Investigation of some dielectric properties of phosphate glasses doped with iron oxides, by a microwave technique

The effects of iron ions on dielectric properties of lithium sodium phosphate glasses were studied by non-usual, fast and non-destructive microwave techniques. The dielectric constant (ε′), insertion loss (L) and microwave absorption spectra (microwave response) of the selected glass system xFe2O3·(1 − x)(50P2O5·25Li2O·25Na2O), being x = 0, 3, 6, … , 15 expressed in mol.%, were investigated. The dielectric constant of the samples was investigated at 9.00 GHz using the shorted-line method (SLM) giving the minimum value of ε′ = 2.10 ± 0.02 at room temperature, and increasing further with x, following a given law. It was observed a gradual increasing slope of ε′ in the temperature range of 25 ⩽ t ⩽ 330 °C, at the frequency of 9.00 GHz. Insertion loss (measured at 9.00 GHz) and measurements of microwave energy attenuation, at frequencies ranging from 8.00 to 12.00 GHz were also studied as a function of iron content in the glass samples.