Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
7545313 | Procedia Manufacturing | 2018 | 6 Pages |
Abstract
The sheet metal forming process is the process of deforming the sheet metal into a desired shape without fracture or excessive localized necking. Variables in sheet metal forming process can be discussed together with formability and test methods. There are many defects occurring during sheet metal forming processes, such as cracking, wrinkling, local necking, buckling etc. The strain measurement in a deformed sheet metal is necessary for measurement comparison. As the thickness of sheet metal is very small as compare to other dimensions of the sheet metal, the sheet metal operation is usually considered as a plane stress problem. The Forming Limit Diagram (FLD) was also determined from surface strain measurement. The FLD is the graph between major strain (â®1) and minor strain (â®2). The Forming Limit Curve (FLC) or the Forming Limit Diagram (FLD) is useful concept for characterizing the formability of sheet metal, which reflects the maximum principal strains that can be sustained by sheet materials prior to the onset of localized necking. Generally there are three methods to establish FLD i.e. theoretical, numerical and experimental. In this paper experimental method is used to develop FLD. For experimental determination of FLD of Mild Carbon steel sheet Limit Dome Height testing is used according to the American Society of Testing Material (ASTM) as published in ASTM E 2218-02. In this paper the procedure of grid marking, punch stretching and strain measurement is used. For punch stretching operation the set up of spherical die and punch has developed on the hydraulic Universal Testing Machine (UTM). The material used for the die and punch is High Carbon High Chromium Steel (HCHCr). For printing the grids on sheet material chemical etching method is used. In this grid making process grids of 5 mm diameter circles printed. For trial experiment the sheet metal sample is stretched at the force of 23 KN. The deformed circles were converted into ellipse and from that deformed ellipse major and minor strains are to be calculated. After that the FLD will give the two different regions of safe and failure zone.
Related Topics
Physical Sciences and Engineering
Engineering
Industrial and Manufacturing Engineering
Authors
Vishwajeet R. Shinge, Uday A. Dabade,