Large scale testing and statistical analysis of dynamic fracture toughness of ductile cast iron

The present paper deals with the experimental determination and statistical analysis of dynamic fracture toughness values of ductile cast iron. KId data from 140 mm thick single edge bend specimens of two dynamic fracture toughness test series on ductile cast iron from heavy-walled castings were analysed.At first, the statistical analysis of data at −40 °C was done based on ASME Code Case N-670 using a two-parameter Weibull distribution function. Weibull analyses of three samples covering different pearlite contents (⩽4%, ⩽9%, ⩽20%) were performed and characteristics of the distribution functions as well as two-sided confidence intervals were calculated. The calculated characteristics show that KId of ductile cast iron decreases with increasing pearlite content.In a second step, the applicability of the Master curve procedure according to ASTM E 1921 to ductile cast iron materials was investigated and it was formally used for statistical analysis of ductile cast iron dynamic fracture toughness data. Although the Master curve method was originally introduced for static fracture toughness data of ferritic steels, the successful individual analyses performed here support the engineering way taken to apply the method to ductile cast iron materials too. The results of both methods, the Master curve procedure and the ASME Code Case N-670, show acceptable congruity. At the same time, it is concluded from the present study that further investigations and experiments are required to improve precision and for verification before the results could be applied within component safety analyses.