We have performed a failure analysis on a monel packing material subjected to sulfidation and sulfide stress cracking after a short period of service in an atmospheric distillation tower containing corrosive gases. Optical macroscopic inspections show that the failed packing material was basically covered with dark scales and corrosion products. Energy dispersive X-ray spectroscopy and X-ray diffraction spectrum show that the corrosion products contain sulfur as the main element along with oxygen indicating that oxidation may have been taken place beside sulfidation. Metallography of the failed samples reveals that cracks exist and were initiated on the surface from defects most likely developed due to the formation of porous and brittle sulfide layer accomplished by hydrogen embrittlement. Although nickel base alloys are an appropriate candidate owing to their high corrosion resistant in corrosive atmospheres, however, presence of H2S, HCl, O2 and naphthenic acid in crude oil lead to reduction in corrosion resistant of the monel 400 alloy.
► Failure analysis of a monel packing material in atmospheric distillation tower. ► Presence of hot corrosive gases leads to SSC and intergranular corrosion in monel 400. ► Formation of nickel and copper sulfides on both surfaces of packing. ► Presence of naphthenic acids in crude oil intensifies sulfidation and SSC.