Abstract

► We document a failure analysis on weld decay in stainless steel due to sensitisation. ► It is less likely that hydrogen affected the failure. ► The electropolishing process could not cause hydrogen embrittlement. ► Recommend introducing coincidence site lattice boundaries for preventing the failure.

Keywords
Related Topics
Physical Sciences and Engineering Engineering Industrial and Manufacturing Engineering
Preview
Failure analysis of a weld-decayed austenitic stainless steel