This paper presents a case study summarising the failure analysis of a high nitrogen stainless steel femoral stem. The failure of the stem occurred after only 4.5 years in service by fatigue failure across the proximal region. The experimental work consisted of a visual inspection, macroscopic inspection, fractography and microscopic examination, surface profilometry and chemical analysis of the material. All metallurgical tests revealed the material to be satisfactory in terms of microstructure, hardness and composition. Inspection of the introducer slots revealed mechanical damage created during surgery to install the stem. The fatigue crack was shown to have initiated from a point of mechanical damage present in one of the introducer slots. This study highlights the detrimental effect of surface damage to initiate fatigue cracks under cyclic loading conditions and the need for greater awareness regarding the possibilities of creating stress raisers such as scratching, scoring and impacts which can lead to premature failure of prostheses.

► This paper presents a case study summarising the failure analysis of a high nitrogen stainless steel femoral stem. ► The failure occurred after 4.5 years in service and initiated from mechanical damage present in an introducer slot. ► This study highlights the detrimental effect of surface damage to initiate fatigue cracks under cyclic loading conditions. ► Need for greater awareness regarding the creation of stress raisers which can lead to premature failure of prostheses.

Related Topics
Physical Sciences and Engineering Engineering Industrial and Manufacturing Engineering
Authors
,