Abstract
⺠(100-x)Li3PS4·xLiAlS2 samples were prepared by a high-energy ball-milling. ⺠The conductivity was increased with increasing the LiAlS2 content. ⺠The maximum conductivity of the sample was 6.0 Ã 10â 4S cmâ 1 at 298 K. ⺠All-solid state batteries were fabricated with the 86.9Li3PS4·13.1LiAlS2 sample. ⺠The battery with TiS2 showed discharge capacity of 185 mA h gâ 1 at room temperature.