Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
7747276 | Solid State Ionics | 2012 | 4 Pages |
Abstract
⺠P2O5 powder was added to 30 mL of 2-methoxyethanol. ⺠This solution was stirred at room temperature until a transparent solution was obtained. ⺠Zirconium tetra-n-butoxide was also added to 30 mL of 2-methoxyethanol, and the two solutions were mixed with P/Zr molar ratios of 0.2 and 4.6. ⺠The zirconium phosphate glass thin films with various phosphorus contents were fabricated by the spin-on-glass technique. ⺠The conductivity of the high-phosphorus-concentration glass thin film was 3.16 Ã 10-5 S/cm at temperatures of up to 350 °C even in the absence of humidity.