Partial crack closure under block loading

Fatigue crack propagation tests under high–low and low–high block loading sequences have been performed in aluminium alloy specimens. The tests were carried out at constant ΔK conditions. Two stress ratios were analysed: R = 0.05 and R = 0.4. Crack closure was monitored in all tests by the compliance technique using a pin microgauge. The observed transient post load step behaviour is discussed in terms of the load change magnitude, ΔK baseline levels and stress ratio. The crack closure level was obtained and compared with the crack growth transients. A good agreement between experimental and predicted crack growth rates is obtained when the partial crack closure effect is properly taken into account. Therefore, plasticity-induced crack closure plays an important role on the load interaction effects observed in aluminium alloys.