Abstract
Localised controlled release of simvastatin from porous freeze-dried chitosan-gelatin (CH-G) scaffolds was investigated by incorporating simvastatin loaded poly-(dl-lactide-co-glycolide) acid (PLGA) microparticles (MSIMs) into the scaffolds. MSIMs at 10% w/w simvastatin loading were prepared using a single emulsion-solvent evaporation method. The MSIM optimal amount to be incorporated into the scaffolds was selected by analysing the effect of embedding increasing amounts of blank PLGA microparticles (BL-MPs) on the scaffold physical properties and on the in vitro cell viability using a clonal human osteoblastic cell line (hFOB). Increasing the BL-MP content from 0% to 33.3% w/w showed a significant decrease in swelling degree (from 1245 ± 56% to 570 ± 35%). Scaffold pore size and distribution changed significantly as a function of BL-MP loading. Compressive modulus of scaffolds increased with increasing BL-MP amount up to 16.6% w/w (23.0 ± 1.0 kPa). No significant difference in cell viability was observed with increasing BL-MP loading. Based on these results, a content of 16.6% w/w MSIM particles was incorporated successfully in CH-G scaffolds, showing a controlled localised release of simvastatin able to influence the hFOB cell proliferation and the osteoblastic differentiation after 11 days.
Related Topics
Physical Sciences and Engineering
Materials Science
Biomaterials
Authors
Piergiorgio Gentile, Vijay Kumar Nandagiri, Jacqueline Daly, Valeria Chiono, Clara Mattu, Chiara Tonda-Turo, Gianluca Ciardelli, Zebunnissa Ramtoola,