This paper deals with the preparation, characterization, and determination of thermal energy storage properties of polyethylene glycol (PEG)/diatomite composite as a novel form-stable composite phase change material (PCM). The composite PCM was prepared by incorporating PEG in the pores of diatomite. The PEG could be retained by 50 wt% into pores of the diatomite without the leakage of melted PEG from the composite. The composite PCM was characterized by using SEM and FT-IR analysis technique. Thermal properties of the composite PCM were determined by DSC analysis. DSC results showed that the melting temperature and latent heat of the composite PCM are 27.70 °C and 87.09 J/g, respectively. Thermal cycling test was conducted to determine the thermal reliability of the composite PCM and the results showed that the composite PCM had good thermal reliability and chemical stability. TG analysis showed that the impregnated PEG into the diatomite had good thermal stability. Thermal conductivity of the composite PCM was improved by adding expanded graphite in different mass fractions. Thermal energy storage performance of the composite PCM was also tested.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideResearch highlights► Polyethylene glycol (PEG)/diatomite composite as novel form-stable phase change materials. ► Thermal energy storage properties, thermal stability and performance of PEG/diatomite composite. ► The melting point and latent heat of the (PEG)/diatomite are 27.70 °C and 87.09 J/g, respectively. ► The composite PCM can decrease indoor air temperature fluctuation due to heat absorption of the PCM.