Enhanced performance of high temperature aluminate cementitious materials incorporated with Cu powders for thermal energy storage

Cementitious materials have been extensively developed in thermal energy storage system of solar thermal power. This paper deals with the volume heat capacity, thermal conductivity, thermal expansion coefficient, and compressive strength of aluminate cementitious thermal energy storage materials with the addition of metal Cu powders. The specimens were subjected to heat-treatment at 105, 350, and 900 °C, respectively. In the heating process, Cu powders gradually oxidized to Cu2O and CuO, providing a so-called mass compensation mechanism for the composite paste. Meanwhile, it indicates that volume heat capacity and thermal conductivity both increase with increasing Cu powders content and decrease with the rising temperature. The optimum thermal properties were obtained at 15 wt% Cu powders loading. In addition, Calorimetric Test, XRD, TG-DSC, and MIP are performed for characterizing the hydration rates, the phases, the mass/heat evolution, and the pore distribution, respectively.