Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
7887642 | Ceramics International | 2018 | 7 Pages |
Abstract
The Nextel⢠440 fiber reinforced nitride matrix (N440/Nitride) composites were fabricated by precursor infiltration and pyrolysis (PIP) route. The results demonstrated that the original N440 fiber had a phase composition of amorphous SiO2 and γ-Al2O3. Its single filament tensile strength was 3.03 GPa (at room temperature), while it dropped to 72.6% and 35.1% at 1200 °C and 1400 °C, respectively. The phase content of N440/Ntride composites was mainly γ-Al2O3 and amorphous BN, as well as mullite phase (formed at > 1100 °C). The composites owned a flexural strength up to 76.0 MPa at room temperature. The stair-stepping decrease in the load-displacement curve and fiber pull-outs in the fracture surface indicated a good fiber/matrix interface and toughness. By heating at 1400 °C, the composites still possessed 67.4% of original bending strength. It was found that the high temperatures caused strong fiber-matrix bonding and severe fiber degradation. The specific heat, CTE and thermal conductivity of the composites were 0.325-0.586 J gâ1 Kâ1, (3.2-4.0) à 10â6 Kâ1 and 0.78-3.47 W mâ1 Kâ1, respectively. The composites possessed a dielectric constant of 4.25-4.35 and loss tangent of 0.004-0.01 at 8-12 GHz. The good overall performances enabled the N440/Nitride composites advanced high-temperature wave-transparent applications.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Duan Li, Bin Li, Yuanyi Zheng, Shitao Gao, Xuejin Yang,