In this study, a triple-layer thermal barrier coating (TBC) of Cu-6Sn/NiCrAlY/YSZ was deposited onto a carbon-fiber reinforced polyimide matrix composite. Effects of different thicknesses of YSZ ceramic top coat and NiCrAlY intermediate layer on microstructural, mechanical and thermal shock properties of the coated samples were examined. The results revealed that the TBC systems with up to 300 µm top coat thicknesses have clean and adhesive coating/substrate interfaces whereas cracks exist along coating/substrate interface of the TBC system with 400 µm thick YSZ. Tensile adhesion test (TAT) indicated that adhesion strength values of the coated samples are inversely proportional to the ceramic top coat thickness. Contrarily, thermal shock resistance of the coated samples enhanced with increase in thickness of the ceramic coating. Investigation of the TBCs with different thicknesses of NiCrAlY and 300 µm thick YSZ layers revealed that the TBC system with 100 µm thick NiCrAlY layer exhibited the best adhesion strength and thermal shock resistance. It was inferred that thermal mismatch stresses and oxidation of the bond coats were the main factors causing failure in the thermal shock test.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
H.R. Abedi, M. Salehi, A. Shafyei,