Abstract
The influence of impact energy and stacking sequence on the damage resistance and Compression After Impact (CAI) strength of Carbon and Glass Fibre Reinforced Plastic (CFRP and GFRP respectively) hybrid laminates is investigated. CAI tests demonstrate that, in comparison to fully CFRP laminates, hybrid laminates show increases in structural efficiency of up to 51% for laminates subject to a 12J impact and 41% for those subject to an 18J impact. Laminates displaying the highest stresses at failure are those that exploit stacking sequences and GFRP content to prevent delaminations from forming close to the outer surface of the laminate during impact. This favourable damage morphology inhibits both sublaminate-buckling-driven delamination propagation and anti-symmetric laminate buckling failures.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Andrew T. Rhead, Shi Hua, Richard Butler,