Ductile failure of metals is often treated as the result of void nucleation, growth and coalescence. Various criteria have been proposed to capture this failure mechanism for various materials. In this study, ductile failure of dual phase steels is predicted in the form of plastic strain localization resulting from the incompatible deformation between the harder martensite phase and the softer ferrite matrix. Microstructure-level inhomogeneity serves as the initial imperfection triggering the instability in the form of plastic strain localization during the deformation process. Failure modes and ultimate ductility of two dual phase steels are analyzed using finite element analyses based on the actual steel microstructures. The plastic work hardening properties for the constituent phases are determined by the in-situ synchrotron-based high-energy X-ray diffraction technique. Under different loading conditions, different failure modes and ultimate ductility are predicted in the form of plastic strain localization. It is found that the local failure mode and ultimate ductility of dual phase steels are closely related to the stress state in the material. Under plane stress condition with free lateral boundary, one dominant shear band develops and leads to final failure of the material. However, if the lateral boundary is constrained, splitting failure perpendicular to the loading direction is predicted with much reduced ductility. On the other hand, under plane strain loading condition, commonly observed necking phenomenon is predicted which leads to the final failure of the material. These predictions are in reasonably good agreement with experimental observations.