| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 7894723 | Corrosion Science | 2016 | 9 Pages |
Abstract
The role of thermally grown α-Fe2O3 on the nucleation of α-Al2O3 during oxidation of binary Fe-Al alloys with 15 and 26 at.%Al at 700 °C was investigated. Surface morphology of the oxide scales indicated direct nucleation of α-Al2O3 preferentially instead of conversion from metastable Al2O3 polymorphs. Oxide scale development over time was also monitored by use of synchrotron X-ray diffraction and Raman spectroscopy. The results showed that the α-Fe2O3 crystal lattice decreases in volume as oxidation progresses, which was found to be consistent with an Al3+ enrichment of α-Fe2O3 as confirmed by the change in relative intensity of α-Fe2O3 Raman peaks.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Pedro Brito, Haroldo Pinto, Aleksander Kostka,