Influence of processing on stability, microstructure and thermoelectric properties of Ca3Co4 − xO9 + δ

Due to high figure of merit, Ca3Co4 − xO9 + δ (CCO) has potential as p-type material for high-temperature thermoelectrics. Here, the influence of processing including solid state sintering, spark plasma sintering and post-calcination on stability, microstructure and thermoelectric properties is reported. By a new post-calcination approach, single-phase materials were obtained from precursors to final dense ceramics in one step. The highest zT of 0.11 was recorded at 800 °C for CCO with 98 and 72% relative densities. In situ high-temperature X-ray diffraction in air and oxygen revealed a higher stability of CCO in oxygen (∼970 °C) than in air (∼930 °C), with formation of Ca3Co2O6 which also showed high stability in oxygen, even at 1125 °C. Since achievement of phase pure high density CCO by post-calcination method in air is challenging, the phase stability of CCO in oxygen is important for understanding and further improvement of the method.