Effect of temper and hydrogen embrittlement on mechanical properties of 2,25Cr–1Mo steel grades – Application to Minimum Pressurizing Temperature (MPT) issues. Part I: General considerations & materials' properties

Standard and Vanadium-alloyed 2,25Cr–1Mo steel grades (EN 10028-2 12CrMo9-10/ASTM A387 gr. 22 and 13CrMoV9-10/ASTM A542 tp. D) are commonly used for the fabrication of heavy pressure vessels for applications in petroleum refining plants.These reactors are made of heavy plates, forged shells, forged nozzles and fittings. They are subjected to thermal cycles (stop and go) and to severe service conditions (high temperatures and high hydrogen partial pressures). A primary concern for end-users is the definition of the Minimum Pressurizing Temperature (MPT) of the equipment. This temperature is the lowest temperature at which the vessel can be repressurized after shutdown and insures no risk of brittle failure of the containment body. The MPT is defined by fracture mechanics and/or CVN approaches and calculations.This first part of the paper presents the impact of thermal aging and exposure to hydrogen on materials' mechanical properties and consequently on the value of MPT.