Synthesis, structure and spectroscopic properties of luminescent GdVO4:Dy3+ and DyVO4 particles

In this work, we focused on the syntheses, structure and spectroscopic properties of GdVO4:Dy3+ and DyVO4 (nano)particles of different sizes and shapes (spherical nanoparticles of 2 nm, 4 nm, and 20 nm in size, nanorods with a few nanometers in diameter and up to 10-20 nm in length and microparticles of 1-8 μm) obtained by four synthetic methods. The size effect on the structure, Raman active modes, and photoluminescence emission intensities was analyzed by X-ray diffraction, Raman and photoluminescence spectroscopy, scanning and transmission electron microscopy, and diffuse reflection spectroscopy. All X-ray diffraction patterns clearly indicated presence of a single tetragonal zircon-type phase; absence of impurity phases indicate that the dopant Dy3+ ions were successfully and uniformly incorporated into the GdVO4 host lattice due to the equal valence and similar ionic radii. Micro-Raman measurements support the XRD measurements and showed Raman-active modes of the REVO4 systems (RE = Gd, Dy). The difference between the two hosts in the diffuse reflectance spectra was observed and it could be attributed to more effective Gd3+ ions on the charge transfer bands and different polarization (compared to bulk material) in smaller nanoparticles. Photoluminescence spectroscopy showed several bands in the visible and near-infrared regions which can be exclusively attributed to the f-f transitions of Dy3+ ions.