| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 7921182 | Materials Chemistry and Physics | 2018 | 7 Pages |
Abstract
This study investigated the failure mechanism of Ag-4Pd wire bonded on Al metallization under chlorine corrosive environments after high temperature storage tests (HTST) and thermal cycle tests (TCT). Results show that as-bonded samples encountered the fastest failure, caused by corrosion of Al metallization accelerated by galvanic corrosion. For HTST samples, the intermetallic compound (IMC) layer was corroded and separated into the upper layer of Ag2Al and Ag3Al and the lower layer of Ag3Al2. The non-continuous Ag3Al2 IMC layers in TCT samples can act as a barrier to inhibit the galvanic corrosion and effectively retard the corrosion rate of Al metallization.
Related Topics
Physical Sciences and Engineering
Materials Science
Electronic, Optical and Magnetic Materials
Authors
Jui-Nung Wang, Yan-Wen Tsau, Fan-Yi Ouyang,