| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 7970726 | Materials Characterization | 2014 | 29 Pages |
Abstract
Aluminum alloy AA6111 and TiAl6V4 dissimilar alloys were successfully welded by high power ultrasonic spot welding. No visible intermetallic reaction layer was detected in as-welded AA6111/TiAl6V4 welds, even when transmission electron microscopy was used. The effects of welding time and natural aging on peak load and fracture energy were investigated. The peak load and fracture energy of welds increased with an increase in welding time and then reached a plateau. The lap shear strength (peak load) can reach the same level as that of similar Al-Al joints. After natural aging, the fracture mode of welds transferred from ductile fracture of the softened aluminum to interfacial failure due to the strength recovery of AA6111.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
C.Q. Zhang, J.D. Robson, O. Ciuca, P.B. Prangnell,