7974725 | Materials Science and Engineering: A | 2016 | 6 Pages |
Abstract
Martensitic transformation in off-stoichiometric Co2VSi Heusler alloy was firstly confirmed in this work. The martensite phase presents an ordered 2M non-modulate D022 structure transformed from L21 Heusler structure. In the Co63.5V17.0Si19.5 alloy, the forward and reverse martensitic transformation temperatures are extremely high which reach up to 683 °C and 693 °C, respectively, higher than most known Heusler-type high-temperature shape memory alloys. And results also indicate that the single martensite phase alloy exhibits a good ductility and strength with the compressive strain of over 15% and strength of about 2300 MPa, respectively. What's more, the recoverable strain being maximal to around 3.1% can be obtained at high temperature (750-800 °C) due to its reverse martensitic transformation.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
Hengxing Jiang, Xiao Xu, Toshihiro Omori, Makoto Nagasako, Jingjing Ruan, Shuiyuan Yang, Cuiping Wang, Xingjun Liu, Ryosuke Kainuma,