Abstract
The tensile tests at high strain rates ranging from 10Â sâ1 to 500Â sâ1 were conducted for the Al/Cu laminated composite produced by asymmetrical roll bonding and annealing. The microstructural evolution after tensile test was observed by SEM, EDX and TEM to analyze the strain rate effect on the laminated composite. It is found that the ultimate tensile strength increases obviously with the rise of strain rate, but the elongation reduces drastically. The deformation-induced twins form in the Cu matrix during the dynamic loading, and the strain-rate strengthening effect promotes the compatible deformation between matrix layers and interfacial interlayer. Thus, a good bonding interface is maintained in the composite after fracture at the strain rate above 100Â sâ1. Some deformation bands form in the matrix layers due to the significant dislocation multiplications and tangles in grain boundaries along the tensile direction in the high strain rate deformation.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
X.B. Li, G.Y. Zu, P. Wang,