Transmission electron microscopy (TEM) is a widely used tool to characterize materials. The required samples need to be electron transparent which should be achieved without changing the microstructure. This work describes different TEM sample preparation techniques of nanostructured CuInS2 thin films on fluorine-doped tin oxide substrates, synthesized solvothermally using lâcysteine as sulfur source. Focused ion beam lamellae, conventional cross section samples and scratch samples have been prepared and investigated. It was possible to prepare appropriate samples with each technique, however, each technique brings with it certain advantages and disadvantages. FIB preparation of solvothermally synthesized CuInS2 suffers from two main drawbacks. First, the whole CuInS2 layer displays a strongly increased Cu content caused by Cu migration and preferential removal of In. Further, electron diffraction shows the formation of an additional CuS phase after Ga+ bombardment. Second, diffraction analysis is complicated by a strong contribution of crystalline Pt introduced during the FIB preparation and penetrating into the porous film surface. The conventional cross sectional CuInS2 sample also shows a Cu signal enhancement which is caused by contribution of the brass tube material used for embedding. Additionally, Cu particles have been observed inside the CuInS2 which have been sputtered on the film during preparation. Only the scratch samples allow an almost artefact-free and reliable elemental quantification using energy-dispersive X-ray spectroscopy. However, scratch samples suffer from the drawback that it is not possible to determine the layer thickness, which is possible for both cross sectional preparation techniques. Consequently, it is concluded that the type of sample preparation should be chosen dependent on the required information. A full characterization can only be achieved when the different techniques are combined.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
Anna Frank, Rasa Changizi, Christina Scheu,