Er2O3 coating by reactive magnetron sputtering: Effect of oxygen supply and erbium pre-layer deposition

The film grows in mixed phase of cubic and monoclinic structures when erbium metal pre-layer is deposited on the P91 steel substrate and in pure monoclinic phase in absence of the pre-layer. Post annealing seems to partially convert monoclinic into cubic phase in the mixed phase coating. Better crystallization and slightly more surface roughness is observed in the sample processed with higher oxygen to argon ratio. DC resistivity is found in 1015 Ω*cm range and it is marginally more in the sample processed with more oxygen. The spectroscopic ellipsometry on these films to obtain optical dielectric properties gives encouraging results in terms of close match of the thickness and roughness values with those obtained from SEM and AFM respectively. Systematic study of optical dielectric property suggests a trend consistent with DC resistivity.