Abstract
The slurry erosion-corrosion and microbial corrosion electrochemical behavior of high-velocity oxygen-fuel (HVOF) sprayed WC-10Co-4Cr cermet coatings and the reference stainless steel 1Cr18Ni9Ti were both investigated. The slurry erosion-corrosion test was performed in a rotating disk rig facility with circulating system using distilled water and 3.5â¯wt% NaCl slurries. The microbial influenced corrosion behavior in the presence of SRB was evaluated by electrochemical measurement. The results showed that WC-10Co-4Cr coating exhibited higher slurry erosion-corrosion resistance compared to the stainless steel 1Cr18Ni9Ti in both distilled water and 3.5â¯wt% NaCl slurries. The evolution of the slurry erosion mechanism of the coatings with the augment of NaCl concentration was cracks and microchipping in distilled water slurry, and a combination of detachment of binder phase, microchipping and fragments in 3.5â¯wt% NaCl slurry. Potentiodynamic polarization and electrochemical impendence spectroscopy (EIS) results showed that the WC-10Co-4Cr coating had a comparable microbial influenced corrosion resistance in seawater with SRB as compared to the stainless steel 1Cr18Ni9Ti.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Sheng Hong, Yuping Wu, Wenwen Gao, Jianfeng Zhang, Yugui Zheng, Yuan Zheng,