In this work, we investigated the long-term oxidation behavior of a Ni-Fe (1:1â¯wt ratio) support for solid oxide fuel cell (SOFC) applications. Ni-Fe supports were obtained through tape casting, high temperature sintering and pre-reducing in 97% H2/N2 (9/91)-3% H2O at 750 and 1000â¯Â°C, respectively. Then the Ni-Fe supports were exposed in simulated anode atmospheres of 97% H2/N2 (9/91)-3% H2O and 75% H2/N2 (9/91)-25% H2O for periods of up to 1000â¯hâ¯at 750â¯Â°C. The samples were examined for mass change, phase and chemical composition, and microstructure evolution during the annealing process. The Ni-Fe supports exposed to H2/N2-3% H2O showed negligible oxidation, while those exposed to H2/N2-25% H2O showed a 4-6% mass increase, due to the fact that a Fe-rich oxide scale was found on the surface of the Ni-Fe alloy particles. Room-temperature conductivity measurements showed that the supports annealed in the two atmospheres maintained sufficiently high conductivity. The results from the current work demonstrate that the porous Ni-Fe support can be well employed in SOFCs, especially metal-supported SOFCs.
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Na Xu, Ming Chen, Minfang Han,