Ho3+/Yb3+ co-doped YNbO4 phosphor was synthesized via a high-temperature solid-state reaction technique. Excitation power density and temperature dependent up-conversion (UC) luminescence properties were systematically investigated. Under 980â¯nm excitation, intense green UC emissions accompanied with weak red and near infrared UC emissions were observed, which were attributed to the transitions of 5S2/5F4â5I8, 5F5â5I8 and 5S2/5F4â5I7, respectively. Varied population paths for generating the green and the red UC emissions were found from the analyses on the temperature and excitation power density dependent UC emissions. It was confirmed that 2-photon processes were responsible for both the green and the red UC emissions at room temperature. However, with an increase in temperature, the green UC emission still kept 2-photon process, and 1.5-photon process for the red UC emission occurred. In addition, the temperature dependent UC luminescence spectra displayed that the luminescence intensity ratio of the red to the green UC emissions was sensitive to both the excitation power density and the sample temperature. Thus, it was concluded that the dependence of the luminescence intensity ratio of the red to the green UC emissions of Ho3+ on temperature might not be suitable for accurate temperature sensing for YNbO4: Ho3+/Yb3+ phosphor.
Related Topics
Physical Sciences and Engineering
Materials Science
Metals and Alloys
Authors
Xin Wang, Xiangping Li, Sai Xu, Lihong Cheng, Jiashi Sun, Jinsu Zhang, Baojiu Chen,