Article ID Journal Published Year Pages File Type
8000377 Journal of Alloys and Compounds 2015 8 Pages PDF
Abstract
In this work a titanium hydride powder is used to elaborate Ti/TiC MMC. Although an additional dehydrogenation operation is required a significant decrease of the sintering temperature is expected with this basis powder. In this context, the behavior of titanium hydride powder mixed with 0, 10 and 20 vol.% TiC reinforcement is studied during densification by free sintering. The effects of particle size, temperature and rate of sintering reinforcement are discussed. The comparison of the TiH2 process with Ti HDH (Hydride Dehydride) and atomized Ti mixture is made with 10 vol.% reinforcement. The results indicate that the sintering temperature is lowered and the final densities achieved are higher if the hydride is used. Interactions between dehydrogenation and sintering mechanisms clearly appear for the higher sintering temperature rate (10 °C/min) and need specific attention to prevent porosity nucleation through hydrogen entrapment.
Related Topics
Physical Sciences and Engineering Materials Science Metals and Alloys
Authors
, , , , , ,