| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 8012453 | Materials Letters | 2018 | 4 Pages |
Abstract
2024 aluminum alloy deposits were produced with wireâ¯+â¯arc additive manufacturing procedure. Solution treatmentâ¯+â¯natural aging processes with different solution treatment temperature were conducted to improve the properties. The microstructure and mechanical properties were investigated. After heat treatment the distributing characteristic of the second phase changed to be dispersive from continuous in as-deposited condition. Solution treatmentâ¯+â¯natural aging process can significantly improve the properties of WAAM 2024 aluminum alloy. With higher solution treatment temperature, the micro hardness, tensile properties and elongation presented an increasing trend. After 503â¯Â°C solution treatmentâ¯+â¯natural aging process, the micro hardness, ultimate tensile strength, yield strength and elongation were 143HV, 497â¯MPa, 330â¯MPa and 16%, respectively, which can nearly meet the applying requirement.
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Zewu Qi, Baoqiang Cong, Bojin Qi, Gang Zhao, Jialuo Ding,