| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 8025653 | Surface and Coatings Technology | 2016 | 22 Pages |
Abstract
W/Ni/Fe alloy coating with different tungsten (W) content were prepared on CuCrZr substrate by cold spray (CS) process. The coating's surface and cross-section morphologies were investigated by scanning electron microscope. Results demonstrated that the CS W alloy coating was compact, voidless, crackless and free from impurities. The cohesive strength of CS W/Ni/Fe alloy coating was higher than 30 MPa. The coating's maximum Vickers hardness was measured to be 528 HV. The minimum porosity of deposit was measured to be 0.1%. Its maximum thickness can reach up to 1.9 mm when graded method was applied. The thermal shock cycles of graded coating can reach up to 330 and 46 at 500 °C and 800 °C respectively.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Min Xia, Peng Huang, Rui-Kun Cu, Chang-Chun Ge,