Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
8037963 | Ultramicroscopy | 2016 | 8 Pages |
Abstract
In this paper, we evaluate and compare doping contrast generated inside the scanning electron microscope (SEM) and scanning helium ion microscope (SHIM). Specialised energy-filtering techniques are often required to produce strong doping contrast to map donor distributions using the secondary electron (SE) signal in the SEM. However, strong doping contrast can be obtained from n-type regions in the SHIM, even without energy-filtering. This SHIM technique is more sensitive than the SEM to donor density changes above its sensitivity threshold, i.e. of the order of 1016 or 1017 donors cmâ3 respectively on specimens with or without a p-n junction; its sensitivity limit is well above 2Ã1017 acceptors cmâ3 on specimens with or without a p-n junction. Good correlation is found between the widths and slopes of experimentally measured doping contrast profiles of thin p-layers and the calculated widths and slopes of the potential energy distributions across these layers, at a depth of 1 to 3 nm and 5 to 10 nm below the surface in the SHIM and the SEM respectively. This is consistent with the mean escape depth of SEs in silicon being about 1.8 nm and 7 nm in the SHIM and SEM respectively, and we conclude that short escape depth, low energy SE signals are most suitable for donor profiling.
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Augustus K.W. Chee, Stuart A. Boden,