Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
8076272 | Energy | 2014 | 7 Pages |
Abstract
A novel composite PCM (phase change material) with PA-SA (palmitic-stearic acid) eutectic mixture as PCM and EG (expanded graphite) as supporting material was prepared. The optimum absorption ratio of PA-SA/EG (Palmitic-stearic acid/expanded graphite) composite PCM was determined as PA-SA:EG = 13:1 (by mass). Scanning electron microscope and Fourier transformation infrared spectroscopy results show that PA-SA was uniformly distributed in the porous network structure of EG due to the physical action. Thermal property and thermal stability of the PA-SA/EG composite PCM were characterized by DSC (differential scanning calorimetry) and TGA (thermogravimetric analysis). DSC results indicated that the melting and freezing temperatures and latent heats of PA-SA/EG were measured as 53.89 °C and 54.37 °C, and 166.27 J/g and 166.13 J/g. TGA test results revealed that PA-SA/EG had a good thermal stability in working temperature range. Thermal cycling test results showed PA-SA/EG had a good thermal reliability after 720 thermal cycles. Thermal conductivity of the composite PCM was measured as 2.51 W/m K, much higher than that of PA-SA. The thermal energy storage and release rates of PA-SA/EG were also increased due to the high thermal conductivity of EG. In conclusion, the prepared PA-SA/EG composite PCM can be acted as a potential material for thermal energy storage due to the acceptable thermal properties, good thermal reliability and stability, high thermal conductivity.
Related Topics
Physical Sciences and Engineering
Energy
Energy (General)
Authors
Nan Zhang, Yanping Yuan, Yanxia Du, Xiaoling Cao, Yaguang Yuan,