Towards graphite-free hot zone for directional solidification of silicon

The reduction of SiC, Si3N4 and transition metals impurities in directionally solidified Si ingots poses one of the crucial challenges in the solar cells production. Particularly strong contamination comes from the graphite parts in the hot zone. Therefore, we selected three massive ceramic materials to replace graphite, developed the novel design of the crucible support and cover and compared the crystals grown in them with ingots from the standard graphite design. The experiments were performed for phosphorus n-doped silicon of G0 size. The ingots were compared with respect to O- and C-content, metal impurities, resistivity and lifetime. The superior performance of TiC relative to other ceramics was observed, particularly due to the lower concentration of substitutional carbon in Si ingot (up to 2.6 times) and the higher minority carrier lifetime of (up to 4.4 times) with narrow red zones.