Facile synthesis, characterization and magnetic property of CuFe12O19 nanostructures via a sol-gel auto-combustion process

Copper hexaferrite (CuFe12O19) nanostructures were prepared by a simple route utilizing maltose-assisted sol-gel process. The morphology, phase structure, composition and purity of nanostructures can be controlled by type of surfactant and also adjusting the Cu:surfactant, Cu:Fe and Cu:reductant ratios. The bean-shape structures are formed in the absence of the surfactant when the molar ratio of Cu:Fe and Cu:reductant are 1:12 and 1:26, respectively. The agglomerated spherical nanoparticles with diameters ranging from 7 to 20 nm are obtained in the presence of triplex, when ratio of Cu:reductant is 1:26. In the absence of surfactant and also in the presence of triplex, the samples are found to be CuFe12O19. When polymer is used, there are still the peaks of CuFe12O19 and also some boad peaks in XRD patterns, because of the small size and encapsulation of nanostructures with polymer. Magnetic measurments show superparamagnetic behavior for the all samples. The Ms for the samples obtained in the presence of polymer shows that the coating of magnetic nanostructures does not always increase Ms. FT-IR frequency bands in the range 463-626, 607 and 542 cm−1 correspond to the formation of metal oxides in ferrites.