Controlled synthesis and microwave absorption properties of Ni0.6Zn0.4Fe2O4/PANI composite via an in-situ polymerization process

The binary composites of conducting polyaniline (PANI) and nickle zinc ferrite were synthesized by an in-situ polymerization process, and the electromagnetic absorption properties of the composites were also investigated. The FT-IR spectra present the peaks of PANI (1562, 1481, 1301, 1109, and 799 cm−1) and the bonds of NiZn ferrite (579 and 390 cm−1), indicating the existence of both NiZn ferrite particles and PANI in the composites. With the increasing ratio of nickle zinc ferrite, the composites distributes in irregular compared with pure PANI and Ni0.6Zn0.4Fe2O4. The TG curves of the pure PANI and PANI/Ni0.6Zn0.4Fe2O4 composites with different molar ratios clearly show the increase percentage of the ferrite in the composites. Furthermore, we found that the excellent electromagnetic absorption properties and wide absorption bandwidth can be achieved by adjusting proper molar ratios Ni0.6Zn0.4Fe2O4 to PANI. The maximum reflection loss of Ni0.6Zn0.4Fe2O4/PANI can reach to −41 dB at 12.8 GHz and the bandwidth exceeding −10 dB can reach to 5 GHz with the absorber thickness of 2.6 mm at the molar ratio of 1:2. This can be attributed to the enhancing magnetic loss and the better impedance matching. Therefore, Ni0.6Zn0.4Fe2O4/PANI ferrite composites can become a new kind of candidate in the field of the microwave absorbing.