Nylon-6/Graphene composites modified through polymeric modification of graphene

The covalent functionalization of graphene oxide (GO) with poly(vinyl alcohol) (PVA) via ester linkages (GO-es-PVA) as well as the characterization of modified graphene based Nylon-6 (PA6) composite prepared by solution mixing techniques was examined. The anchoring of PVA chains on GO sheets was confirmed by XPS and FTIR measurements. The resulting functionalized sample became soluble in formic acid, allowing solution-phase processing for preparation of PA6/GO composites. Answering to the efficient polymer-chain grafting, a homogeneously dispersion of GO sheets in PA6 matrix and a dramatic improvement of interface adhesion between nanosheets and matrix were observed in PA6/GO-es-PVA composites by SEM and TEM. The depressed crystallization of PA6 chains in PA6/GO-es-PVA composites was investigated by their DSC and XRD results.