Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
822236 | Composites Science and Technology | 2008 | 8 Pages |
Vinyl ester (VE) resins with a bimodal distribution of molecular weights were prepared via methacrylation of epoxy monomers. Bimodal VE resins and neat polymers had viscosities and mechanical properties similar to that of commercial resins. E-glass composites were prepared and also found to have similar mechanical and thermo-mechanical properties relative to composites fabricated using commercial resins. However, the fracture toughness of the bimodal resins was superior to that of the commercial resins partially as a result of increased molecular relaxations that were manifested in a broader glass transition. Overall, bimodal resins allow for the use of low styrene content (∼33 wt%), while maintaining excellent thermal, mechanical, and fracture properties for the neat resins and composites.