Dosimeter properties of MgO transparent ceramic doped with C

We have investigated the photoluminescence (PL), scintillation and thermally-stimulated luminescence (TSL) dosimeter properties of MgO ceramic doped with C ions (0.001, 0.01 and 0.1%). The samples were synthesized by a Spark Plasma Sintering (SPS) technique. The PL emission peaks appeared around 400 and 750 nm in all the samples. The PL decay time constants at 400 nm were ∼10 and ∼100 ns which were on the typical order of F+ center in the undoped MgO. The scintillation emission peaks were detected at 330, 400 and 750 nm under X-ray irradiation. The TSL glow curves showed the ∼250 °C peak in 0.1% C-doped sample. The TSL response was confirmed to be linear to the irradiation dose over the dose range from 0.1 to 1000 mGy. As a result, the sensitivity of MgO was improved by C-doping.