•Increasing cement content in rubberized cement-stabilized mixtures generates greater tensile strength.•Reduction in cement-stabilized mixtures strength due to rubber inclusion is more obvious at high cement content.•Toughness improvement and stiffness reduction confirm more ductile behaviour due to rubber inclusion at all cement contents.•Cracks in rubberized cemented mixtures propagate through the rubber particles at all cementation levels.•Performance of rubberized cemented mixes depends on the relative stiffness between rubber and surrounding matrix.
An investigation and comparison is made of the effect of cement content on the performance of rubberized cement-stabilized aggregate mixtures and on cement-stabilized aggregate mixtures containing no rubber (RCSAMs and CSAMs). These materials are intended to be used as a base course for pavement structures. Three cement contents (3%, 5%, and 7% by dry weight of aggregate) were investigated. Rubberized mixtures were manufactured by replacing 30% of one aggregate fraction that has a similar gradation of crumb rubber. Performance was evaluated under static and dynamic testing. The investigated properties are unconfined compressive strength, indirect tensile strength, indirect tensile static modulus, toughness, dynamic modulus of elasticity, dynamic modulus of rigidity and dynamic Poisson's ratio. Increasing cement content increases strength of both types of mixtures, especially in the CSAMs. It is found that using crumb rubber at low cement content is more feasible than with high cement contents. Stiffnesses increased for both types of mixture as cement content increased but decreased on incorporation of crumb rubber. Energy absorption capacity was inversely related to stiffness. Mesostructural investigation revealed that the cracks were propagated through the rubber particles for all cement contents.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slide