Effects of indium addition on properties and wettability of Sn–0.7Cu–0.2Ni lead-free solders

•Addition of In to solder decreases melting temperature and broadens melting range.•The optimal CET of solder alloy to match with copper substrate is 17.51 × 10−6/°C.•Corrosion rate of solder decreases with In increasing.•Addition of In improves the wettability of lead-free solder.•The hardness of solder decreases with In increasing.

This paper reports the investigation on indium addition into Sn–0.7Cu–0.2Ni lead-free solder to improve its various performances. The effects of indium addition on melting temperature, coefficient of thermal expansion (CTE), wettability, corrosion resistance and hardness of the solder alloys were studied. The results showed that when the addition of indium was ⩽0.3 wt.%, the change in melting temperature of Sn–0.7Cu–0.2Ni–xIn solders was negligible, but the melting range of the solder alloy increased. The CTE and spreading area of Sn–0.7Cu–0.2Ni–xIn solders on copper both increased with the addition of indium. An optimal CTE was 17.5 × 10−6/°C by adding 0.3 wt.% indium. At this concentration, the spreading area of solder on copper was about 15.6% larger than that of Sn–0.7Cu–0.2Ni indium-free solder. The corrosion resistance also increased with the addition of indium increasing, and the corrosion rate of Sn–0.7Cu–0.2Ni–0.3In solder was reduced by 32.8% compared with Sn–0.7Cu–0.2Ni alloy after 14 days in 5% hydrochloric acid solution at room temperature. However, a decrease of 11.7% in hardness of the solder was found when 0.3 wt.% indium was added.