| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 832395 | Materials & Design (1980-2015) | 2009 | 7 Pages |
Abstract
Sulfide Stress Cracking (SSC) of API-X100 high strength low alloy steel was evaluated in NACE solution “A” at room temperature. The corrosion rate, utilizing electrochemical polarization techniques, in the solution was 97 mpy. Proof ring testing, per NACE TM-0177, generated an SSC threshold stress value of 46% of yield strength. SSC susceptibility was caused by the high corrosion rate which formed corrosion pits that acted as crack initiation sites on the metal surface and provided more hydrogen to migrate into the steel. In addition, the X100 inhomogeneous microstructure provided a high density of hydrogen traps which promoted hydrogen embrittlement.
Related Topics
Physical Sciences and Engineering
Engineering
Engineering (General)
Authors
M. Al-Mansour, A.M. Alfantazi, M. El-boujdaini,