Suitability of Thiel embalmed tendons for biomechanical investigation

The current study investigates the effects of Thiel embalming on human digitorum profundus tendons (FDP) from fresh-frozen and Thiel embalmed cadavers. Cross-sectional area was measured at pre-load, samples were preconditioned and then ramped at a constant strain-rate to failure. Thiel preserved tendons had statistically lower failure stress with median of 38 MPa compared to fresh frozen samples with median of 60 MPa (p-value = 0.048) and trended to a decreased tangential modulus. To overcome limited donor number and masking factors of age, gender, and time embalmed, we also performed experiments in rat tail tendon fascicle. Similar quasi-static ramp to failure tests were performed with control and Thiel treated sample pairs. Similar differences were observed to those found as in human FDP, however these trends were statistically significant. In both tendons, Thiel preserved samples demonstrated altered failure characteristics, indicating a different collagen fiber/collagen network failure mechanism most likely due to partial denaturing by boric acid in Thiel solution. In conclusion, Thiel embalmed tendons did not faithfully represent the biomechanical characteristics of fresh frozen tendons.